Sumico Metal is one of the biggest Manufacturer , Supplier & Exporters of excellent quality API 5L X65 PSL 2 Pipes. We manufacture these Seamless Steel Pipes using extreme grade of raw material. These are used for building construction and industries like oil, petrochemical, refinery and many more. We have been supplying high quality API 5L X 65 PSL 2 with most advance technology and with most reliable quality. We offer these Pipes in varied grades and technical specifications to our esteemed clients. We offer them at industry leading prices.
| Sizes (Seamless) | : | 1/2” NB - 60” NB |
| Sizes (ERW) | : | 1/2” NB - 24” NB |
| Sizes (SAW) | : | 16” NB - 100” NB |
| Sizes LSAW/DSAW | : | 16'OD TO 54' OD (8 MM TO 50 MM THK) |
| Wall Thickness | : | SCH10,SCH20,SCH30,STD,SCH40,SCH60,XS,SCH80,SCH100,SCH120,SCH140,SCH160,XXS DIN, JIS standard thickness |
| Dimensions | : | All Pipe is manufactured and inspected/tested to the relevant standards including ASTM, ASME, API. |
| Additional Testing | : | NACE MR0175, NACE TM0177, NACE TM0284, HIC TEST, SSC TEST, H2 SERVICE, IBR, etc. |
| Mass fraction, based upon heat and product analysis % maximum | CARBON EQUIVALENT a | ||||||||||
| % MAXIMUM | |||||||||||
| Cb | Si | Mnb | P | S | V | Nb | Ti | Other | CEIIW | CEPcm | |
| SEAMLESS & WELDED PIPES | |||||||||||
| L450Q or X65Q | 0.18f | 0.45f | 1.7f | 0.025 | 0.015 | g | g | g | h | 0.43 | 0.25 |
| WELDED PIPE | |||||||||||
| L450M OR X65M | 0.12f | 0.45f | 1.6f | 0.025 | 0.015 | g | g | g | h | 0.43 | 0.25 |
| Y.S | T.S | ELONGATION |
| Mpa(psi) | Mpa(psi) | |
| min | min | min |
| 450(65 300) | 600(87 000) | 23% |
| IMPACT TEST | |
| AVG. ABSORBED ENERGY | IND. ABSORBED ENERGY |
| Min.(joules) | Min.(joules) |
| 27 | 20 |
• Unless otherwise agreed, the sum of th niobium & vanadum concentrations shall be = 0.06%
• Unless otherwise agreed, 0.50% maximum for copper, 0.30% maximum for nickel, 0.30% maximum for chromium, & 0.15% maximum for molybdenum.
• The sum of th niobium & vanadum & titanium concentrations shall be =0.15%
• Unless otherwise agreed, 0.50% maximum for copper, 0.30% maximum for nickel, 0.30% maximum for chromium, & 0.15% maximum for molybdenum.
• Unless otherwise agreed g unless otheriwse agreed the sum of th niobium & vanadum & titanium concentrations shall be =0.15%