We are one of the leading Manufacturers, Supplier and Exporters of API 5L X46 PSL 1 Pipes. We are exclusively trusted by clients for providing the premium Carbon Steel Stainless Pipes within stipulated timeframe and at affordable price. we can also offer information on mechanical & corrosion properties and lengths on request. All products are industry-standard conforming to or exceeding API, ASTM, ASME, ANSI and other national and international standards. We offer these pipes in different dimentions, shapes, sizes, material specifications as per clients own requirement.
| Sizes (Seamless) | : | 1/2” NB - 60” NB |
| Sizes (ERW) | : | 1/2” NB - 24” NB |
| Sizes (SAW) | : | 16” NB - 100” NB |
| Sizes LSAW/DSAW | : | 16'OD TO 54' OD (8 MM TO 50 MM THK) |
| Wall Thickness | : | SCH10,SCH20,SCH30,STD,SCH40,SCH60,XS,SCH80,SCH100,SCH120,SCH140,SCH160,XXS DIN, JIS standard thickness |
| Dimensions | : | All Pipe is manufactured and inspected/tested to the relevant standards including ASTM, ASME, API. |
| Additional Testing | : | NACE MR0175, NACE TM0177, NACE TM0284, HIC TEST, SSC TEST, H2 SERVICE, IBR, etc. |
| Mass fraction, based upon heat and product analysis a | ||||||
| SEAMLESS PIPE | ||||||
| C | Mn | P | V | Nb | Ti | |
| maxb | maxb | max. | max. | max. | max. | max. |
| 0.28 | 1.20 | 0.030 | 0.030 | c,d | c,d | d |
| WELDED PIPE | ||||||
| 0.26 | 1.20 | 0.030 | 0.030 | c,d | c,d | d |
| Y.S | T.S | ELONGATION |
| Mpa(psi) | Mpa(psi) | |
| min | min | min |
| 245(35 500) | 415(60 200) | 28% |
• 0.50% maximum for copper, 0.50% maximum for nickel, 0.50% maximum for chromium, and 0.15% maximum for molybdenum.
• For each reduction of 0.01% below the specified maximum concetration for carbon, an increase of 0.05% above the specified maximum concentration for manganese is permissible, up to a maximum of 1.65%
• Unless otherwise agreed, the sum of the niobium and vanadium contents shall be ≤0.06%.
• The sum of the niobium ,vanadium and titanium concentratons shall be ≤0.06%.
• Unless otheriwse agreed.
• Unless otherwise agreed, the sum of niobium, vanadium and titanium concentrations shall be ≤ 0.15%